Different fibers from both natural as well assynthetic category can be used as geotextiles for various applications.


NaturalFibers:


Naturalfibers in the form of paper strips, jute nets, wood shavings or wool mulch arebeing used as geotextiles. In certain soil reinforcement applications,geotextiles have to serve for more than 100 years. But bio-degradable naturalgeotextiles are deliberately manufactured to have relatively short period oflife. They are generally used for prevention of soil erosion until vegetationcan become properly established on the ground surface. The commonly usednatural fibers are:


  1. Ramie
  2. Jute


Ramie:


Theseare subtropical bast fibers, which are obtained from their plants 5 to 6 timesa year. The fibers have silky luster and have white appearance even in theunbleached condition. They constitute of pure cellulose and possess highesttenacity among all plant fibers.


 

Jute:


This is a versatilevegetable fiber which is biodegradable and has the ability to mix with the soiland serve as a nutrient for vegetation. Their quick biodegradability becomesweakness for their use as a geotextile. However, their life span can beextended even up to 20 years through different treatments and blending. Thus, itis possible to manufacture designed biodegradable jute geotextile, havingspecific tenacity, porosity, permeability, transmissibility according to needand location specificity. Soil, soil composition, water, water quality, waterflow, landscape etc. physical situation determines the application and choiceof what kind of jute geotextiles should be used.

 

In contrast to synthetic geotextiles, though jute geotextileas are less durable but they also have some advantages in certain area to be used particularly in agro-mulching and similar area to where quick consolidation are to take place. For erosion control and rural road considerations, soil protection from natural and seasonal degradation caused by rain, water, monsoon, wind and cold weather are very important parameters. Jute geotextiles, as separator, reinforcing and drainage activities, along with topsoil erosion in shoulder and cracking are used quite satisfactorily. Furthermore, after degradation of jute geotextiles, lignomass is formed, which increases the soil organic content, fertility, texture and also enhance vegetative growth with further consolidation and stability of soil.

Synthetic Fibres:


The four main synthetic polymers most widely used as the raw material for geotextiles are polyester, polyamide, polyethylene and polypropylene. The oldest of these is polyethylene which was discovered in 1931 by ICI. Another group of polymers with a long production history is the polyamide family, the first of which was discovered in 1935. The next oldest of the four main polymer families relevant to geotextile manufacture is polyester, which was announced in 1941. The most recent polymer family relevant to geotextiles to be developed was polypropylene, which was discovered in 1954. The commonly used natural fibers are:


  1. Poly amides
  2. Polyesters
  3. Polyethylene
  4. Polypropylene
  5. Polyvinyl chloride
  6. Ethylene copolymer bitumen
  7. Chlorinated poly ethylene


Poly Amides (PA):


There are two most important types of polyamides, namely Nylon 6 and Nylon 6,6 but they are used very little in geotextiles. The first one an aliphatic polyamide obtained by the polymerization of petroleum derivative ε-caprolactam. The second type is also an aliphatic polyamide obtained by the polymerization of a salt of adipic acid and hexamethylene diamine. These are manufactured in the form of threads which are cut into granules. They have more strength but less moduli than polypropylene and polyester. They are also readily prone to hydrolysis.


Polyesters (PET):

 

Polyester is synthesized by polymerizing ethylene glycol with dimethyle terephthalate or with terephthalic acid. The fiber has high strength modulus, creep resistance and general chemical inertness due too which it is more suitable for geotextiles. It is attacked by polar solvent like benzyl alcohol, phenol, and meta-cresol. At pH range of 7 to 10, its life span is about 50 years. It possesses high resistance to ultraviolet radiations. However, the installation should be undertaken with care to avoid unnecessary exposure to light.

Polyethylene (PE):

 

Polyethylene can be produced in a highly crystalline form, which is an extremely important characteristic in fiber forming polymer. Three main groups of polyethylene are Low density polyethylene (LDPE, density 9.2-9.3 g/cc), Linear low density polyethylene (LLDPE, density 9.20-9.45 g/cc) and High density polyethylene (HDPE, density 9.40- 9.6 g/cc).


Polypropylene (PP):


Polypropylene is a crystalline thermoplastic produced by polymerizing propylene monomers in the presence of stereo-specific Zeigler- Natta catalytic system. Homo-polymers and copolymers are two types of polypropylene. Homo polymers are used for fiber and yarn applications whereas co-polymers are used for varied industrial applications. Propylene is mainly available in granular form.


Both polyethylene and polypropylene fibers are creep prone due to their low glass transition temperature. These polymers are purely hydrocarbons and are chemically inert. They swell by organic solvent and have excellent resistance to diesel and lubricating oils. Soil burial studies have shown that except for low molecular weight component present, neither HDPE nor polyethylene is attacked by micro-organisms.


Polyvinyl chloride (PVC):


Polyvinyl chloride is mainly used in geo membranes and as a thermo plastic coating materials. The basic raw materials utilized for production of PVC is vinyl chloride. PVC is available in free- flowing powder form.


Ethylene copolymer Bitumen (ECB):


Ethylene copolymer bitumen membrane has been used in civil engineering works as sealing materials. For ECB production, the raw materials used are ethylene and butyl acrylate (together forming 50-60%) and special bitumen (40-50%).


Chlorinated Polyethylene (CPE):


Sealing membranes based on chlorinated poly ethylene are generally manufactured from CPE mixed with PVC or sometimes PE. The properties of CPE depend on quality of PE and degree of chlorination.